| Chine | Japon | ÉTATS-UNIS | Allemagne | Dureté |
| OCr18Ni9 | SUS304 | AISI304 | 1.4301 | HRC 25-39 |
| 00Cr19Ni10 | SUS304L | AISI304L | 1.4307 | HRC 25-39 |
| 0Cr17Ni12Mo2 | SUS316 | AISI316 | 1.4401 | HRC 25-39 |
| 0Cr19Ni12Mo2 | SUS316L | AISI316L | 1.4404 | HRC 25-39 |
| 3Cr13 | 420J2 | AISI420 | 1.4028 | HRC 48-58 |
| 4Cr13 | - | AISI420C | 1.3541, 1.4034 | HRC52-56 |
| 9Cr18 | - | AISI440 | HRC57-61 | |
| 9Cr18Mo | SUS440C | AISI440C | 1.4125 | HRC58-64 |
| Matériau | COMPOSITION CHIMIQUE % | ||||||||
| C | Si | Mn | P | S | Ni | CR | Mo | TI | |
| AISI304 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 8.0-11.0 | 18-20 | ||
| AISI304L | ≤0.03 | ≤1.0 | ≤2.00 | ≤0.045 | ≤0.03 | 9.0-12.0 | 18-20 | ||
| AISI316 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.03 | 10.0-14 | 16.0-18.5 | 2.0-3.0 | |
| AISI316L | ≤0.030 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 10.0-14 | 16.0-18 | 2.0-3.0 | |
| AISI420(3Cr13) | 0.26-0.35 | ≤1.0 | ≤1.0 | ≤0.04 | ≤0.035 | ≤ ≤ ≤ 0.60 % | 12.0-14.0 | ||
| AISI420C(4Cr13) | 0.36-0.45 | ≤0.60 | ≤0.8 | ≤0.035 | ≤0.03 | ≤0.6 | 12.0-14.0 | ||
| AISI440 (9Cr18) | 0.9-1 | ≤0.8 | ≤0.8 | ≤0.035 | ≤0.80 | ≤0.60 | 17.0-19.0 | ≤0.75 | |
| AISI440C (9Cr18Mo) | 0.9-1 | ≤0.8 | ≤0.8 | ≤0.035 | ≤0.03 | ≤0.60 | 16.0-18.0 | ≤0.75 | |
| Grade : G10 à G1000 | |||||
| Grade | diamètre de la bille | sphérique | surface | diamètre du lot | boule nomainale |
| variation | déviation | rugosité | variation | tolérance de déviation | |
| VDWS | SPH | RA | Vdwl | TDN | |
| pas plus | |||||
| μm | |||||
| 10 | 0.25 | 0.25 | 0.02 | 0.5 | * |
| 16 | 0.4 | 0.4 | 0.025 | 0.8 | * |
| 20 | 0.5 | 0.5 | 0.032 | 1 | * |
| 24 | 0.6 | 0.6 | 0.04 | 1.2 | * |
| 28 | 0.7 | 0.7 | 0.05 | 1.4 | * |
| 40 | 1 | 1 | 0.06 | 2 | * |
| 60 | 1.5 | 1.5 | 0.08 | 3 | * |
| 100 | 2.5 | 2.5 | 0.1 | 5 | ±12.5 |
| 200 | 5 | 5 | 0.15 | 10 | ±25 |
| 500 | 12.5 | 12.5 | * | 25 | ±50 |
| 1000 | 25 | 25 | * | 50 | ±125 |